OLKLIN®-OLCI
Oil Line Corrosion Inhibitor
Description:
The corrosion typically encountered in the transport of a fluid containing one or more fluid (corrosion agents) is flow-induced corrosion. In the case of flow-induced corrosion, the degree of corrosion that occurs is generally depend on a variety of factors like corrosiveness of the fluid itself, the metallurgy of the pipeline and the shear rate, temperature, and pressure of the fluid.
A corrosion inhibitor is frequently introduced into the fluid to reduce the rate of corrosion of the metal vessel, pipeline and/or equipment used to store and transport the fluid.
Chemical Composition:
It is composition of organic specified amines with dispersant.
Specification:
Property | OLKLIN-OLCI |
---|---|
Color | Light yellow to Dark brown viscous liquid |
Specific gravity | 1.00-1.05 |
Solubility | Soluble in water, sea water, & formation water in test proportion |
Physical State:
The material, will be free flowing, homogenous liquid free from visible impurities and suspended solids.
Compatibility & Emulsification Test:
The material will be compatible with crude oil mix(140 ml. of crude oil with 60 ml of AR grade Xylene and brine corrodant, shall not form an emulsion at 24 ± 2°C interface sludge pad thickness will not be more than 5% after five hours.
Stability Test:
The material shall be heated in a well sealed glass stopper measuring cylinder at 80 ± 2°C, for 2 hrs. in laboratory oven. Neither precipitation nor heterogeneous layers shall be observed, on cooling at ambient temperature and mixing after one hour.
Test Conditions:
Corroding Media:
- It consists of 3.2 % Sodium Chloride (LR) solution in distilled water having dissolved Carbon Dioxide content in the range of 1250 +/- 50 ppm at 24°C.
- Take 140 ml. untreated crude oil, and 60 ml. of Xylene (AR) to crude oil.
- The ratio of (a) and (b) shall be 90 : 10 and total volume shall be 150 ml.
Metal Coupons:
The coupons shall be of API 5L – Grade B steel with approx size of 30x25x3-4mm of thickness (total surface area of all sides taken together shall be around 18 +/- 2 cm2). The surface finish shall be to 300 emery grit free pits & scratches.
Test Temperature:
50 ± 2°C.
Corrosion Inhibitor Dose:
35 ppm (W/V).
Exposure Period:
168 hrs. for static test / 24 hrs. for dynamic test.
Test results:
80 % (min) for static and dynamic test with coupons free from pits, scratches on visual inspection.
Handling & Precautions:
Safe to handle. Do not take internally.